Description

Desription of Refractory Mortar:

1.Silica Mortar

Silica refractory mortar is widely used for high temperature industrial equipment such as coke ovens, hot blast stoves, glass kilns, insulating silica bricks, etc. It has the advantages of high refractoriness, high refractoriness under load, reasonable bonding time and so on.

silica mortar.jpg

2.Alumina-silicate Mortar

Alumina-silicate mortar has the characteristics of high bonding strength, stable overall masonry structure, good air tightness, good chemical stability, and long service life. It has good workability during use and small shrinkage after burning.

$alumina-silicate Refractory Mortar.jpg$

3.Alkaline Mortar

Alkaline mortar is composed of magnesium oxide or magnesium oxide and calcium oxide. It has the characteristics of high refractoriness, strong resistance to alkaline slag, high bonding strength and good sealing performance.

alkaline mortar.jpg

4.SiC & C Mortar

SiC mortar has the characteristics of high refractoriness and strong adhesion that general refractory mortar should have. Besides, it has good volume stability, good alkali resistance, good thermal shock resistance and low thermal expansion.

SIC&C mortar.jpg

Technique Data

Technique Data of Refractory Mortar:

1.Silica Mortar

Item		Specification
		GNR94	GNJ94	GNB94	GNB96
SiO₂ %		≥94	≥94	≥94	≥96
Al₂O₃ %		/	/	≤1	≤0.6
Fe₂O₃ %		≤1.0	/	≤1.0	≤0.7
Refractoriness, ℃		≥1680	≥1660	≥1700	≥1720
Cold Flexural Bonding Strength, MPa	Drying at 110℃	≥1.0	≥1.0	≥0.8	≥0.8
	1400℃×3h	≥2.0	≥2.0	≥0.8	≥0.5
0.2MPa RUL, T₂ ℃		≥1580	≥1550	≥1600	≥1620
Bonding Time, min		1~2	1~2	2~3	2~3
Particle Size, %	＜2mm	100	100	100	100
	＞1mm	≤1	≤3	≤2	≤2
	＜0.074mm	≥60	50~70	≥60	≥60

2.Alumina-silicate Mortar

Item		Specification
		LN65	LN75	LN65P	LN75P	GN85P	GN90P
Al₂O₃ %		≥65	≥75	≥65	≥75	≥85	≥90
Refractoriness, ℃		≥1760	≥1780	≥1780	≥1780	≥1780	≥1800
Cold Flexural Bonding Strength, MPa	Drying at 110℃	≥1	≥1	≥2	≥2	≥2	≥2
	1400℃×3h	≥4	≥4	≥6	≥6	/	/
	1500℃×3h	/	/	/	/	≥6	≥6
0.2MPa RUL T₂ ℃		/	/	≥1400		≥1600	≥1650
PLC, %	1400℃×3h	-5~+1				/
	1500℃×3h	/				-5~+1
Bonding Time, min		1~3
Particle Size, %	＜1mm	100
	＞0.5mm	≤2
	＜0.074mm	≥50				≥40

3.Alkaline Mortar

Item		Specification
		MN91	MN95	MN97	MLN70	MLN80
MgO %		≥91	≥95	≥97	≥70	≥80
Al₂O₃ %		/			8~20	5~10
Cold Flexural Bonding Strength, MPa	Drying at 110℃	≥1.5	≥1.5	≥1.5	≥1.5	≥1.5
	1500℃×3h	≥3.0	≥3.0	≥3.0	≥3.0	≥3.0
PLC, % 1500℃×3h		-4~+1			-4~+1
Bonding Time, min		1~3			1~3
Particle Size, %	＜1mm	100
	＞0.5mm	≤2
	＜0.074mm	≥60

4.SiC & C Mortar

Item		Specification
		SCN	TN-1	TN-2	TN-3
SiC %		≥85	/	/	/
Fixed Carbon, %		/	≥50	≥55	≥58
Ash, %		/	≤7	≤5	≤2
Volatile, %		/	≤43	≤40	≤40
Flexural Bonding Strength, MPa	200℃×24h	≥2(110℃×12h)	/	8	8
	600℃×3h	≥9(1400℃×3h)	/	1	2.5
Bonding Time, min		1~3	/	/	/
Bulk Density, g/cm³		≥1.7	/	/	/
Seam, mm		/	≤1	≤1	≤1

Project Cases

The Project of Tsinergy

Taikang Project

The Project of Henan Shouchuang Group

Inner Mongolia Project

Yanzhou Project

Yingcheng City Project

Monyin Project

The Project of Chinese Academy of Sciences

Domestic site

Overseas sites